Sintering analysis of NdFeB materials

Résumé

NdFeB magnets present high magnetocrystalline anisotropy that leads to outstanding magnetic properties. This anisotropy is also present during the sintering and plays a role into the mechanisms driving the densification. Sintering was studied along and perpendicular to the easy magnetization axis for an optimized thermal cycle leading to high magnetic properties and full densification. The parallel strain rate is significantly lower than the perpendicular strain rate, especially at low temperature . The sintering kinetics at high temperature would be mainly controlled by solid state diffusion with a high apparent activation energy (450-474kJ/mol).
Fichier principal
Vignette du fichier
REPM2014 Brice Hugonnet.pdf (1.66 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-04925176 , version 1 (01-02-2025)

Identifiants

  • HAL Id : hal-04925176 , version 1

Citer

Brice Hugonnet, Grégory Largiller, F. Servant, Cyril Rado, Jean-Michel Missiaen. Sintering analysis of NdFeB materials. REPM14 - 23rd Rare Earth And Future Permanent Magnets And Their Applications International Workshop, Aug 2014, Annapolis, United States. ⟨hal-04925176⟩
0 Consultations
0 Téléchargements

Partager

More